分散染料牢度问题：大分子染料的牢度好 还是小分子染料牢度好?

如果是做轧染,染液中要加入适量的扩散剂、渗透剂和抗泳移剂.化料时注意不要太高温,20-40摄氏度的水比较合适,助剂通常在最后加入,而且要一直保持搅拌状态；如果是做浸染,染液中要加入适量的匀染剂,可以热水化料,但水温也不要太高,60-80摄氏度比较合适.

分散染料 题usekuai
,阳离子染料,
直接染料,
活性染料,
酸性染上染布料

第一,尽量选用耐温高的分散染料
第二,染色后加强还原清洗,洗掉浮色,减少热迁移
第三,定型温度适当控制,不要太高

ECO是染料名称,300应该是300%,说的是力份,和ECT黑 300%类似

In this article, with more than 30 pieces of silk dyeing with disperse dyes with different structures, filter by measuring its rate of dyeing dyes, and determination of its promotion, discovery of Longsheng group in the production of heat-UN-SE and EE series of disperse dyes have good lifting. Simultaneous determination of dispersion rate of dyeing curve of Red jade S-2GFL, found in 95, 90 ° c under the conditions of dyeing, dyeing balance when 20 MHz respectively, it's added o to join the slight increase in the rate in the early, but on balance would not seriously affect rate of dyeing. 1:1 standard color depth by measuring the color fastness of dyed samples found that rubbing fastness of disperse dyes on silk is better, but weak washing fastness, will be the biggest technology challenges of silk dyeing with disperse dyes.

分散染料本身就不溶于染液,一般配制染液时添加一些分散剂,增加在水溶液中的溶解性,你过滤没用的只会浪费染料(染料合格的话).其次你染色温度有没有达到涤纶染色温度(玻璃化温度以上).

保险粉是一种强还原剂,很多染料的母体结构中都含有偶氮不饱和双键,而这种不饱和双键就是染料的发色基团.保险粉能破坏掉这种共轭性的不饱和双键,使染料褪色.但是分散染料绝大多数都不是这种结构,而是蒽醌共轭结构,保...

分散染料没有固色剂的,要提高牢度,只有提高染色温度和延长染色时间.再就是染色之后充分水洗,把可能脱落的染料都在洗涤过程中洗掉,日后就很少掉色了.

-N=N-在光照下会发生构型变换：
R1 /R2 R1
N=N ----> N=N
R2

涤纶纤维属于疏水性纤维,故水溶性染料对其上染率极低.分散染料染涤纶的原理是在高温高压下涤纶分子链间隙打开,分散染料小分子分散到这些间隙中,在冷却时,间隙闭合,这些染料小分子就被封存在涤纶分子链间,形成染料的固着.所以涤纶一定用分散染料染.

升温速度,上染速率,PH值,助剂,都有关系.

分散染料部分染料会过敏,致癌,就算无毒的分散染料,粉末吸入也对人身体有害
如果你是担忧衣服问题,建议买回来先洗洗

分散染料在水中的分散状态是不稳定的,会因时间、温度及染浴中其他物质的影响而发生变化.其中的一种重要现象是晶体的增长.染料厂虽然力图使染料粒子大小均匀,但实际上是很难办 到的,一般都存在差异.在溶解时,优先得到溶解的是颗粒较小的染料,而大颗粒的染料却吸收从过饱和溶液中结晶出来的染料,结果是晶体逐渐增加.通过周期性的升 温和冷却,这种现象不仅加速而且更为剧烈在实际染色过程中,由于染浴中的染料不断为涤纶染着而减少,所以晶体增长情况并没有这样严重.但在染深色时,染浴中存在着相当数量的染料,如果染浴温度不是逐渐下降而是突然冷却,这种饱和的染浴中已溶解的染料就会在少量还没有溶解的染料粒子周围结晶出来.从实践中发现,染浴中的分散剂能起稳定作用,抑制染料粒子的增长.