微乳液属于化学的哪个分支,配制具体方法?

微乳液法通常是需要使用表面活性剂,将两种互不相溶的溶剂形成宏观看来均一稳定的液体（实际上并不是溶液）,包括W/O和O/W型（油包水或水包油）.由于形成的液滴非常小,相当于一个个微型的反应器.在这个微型反应器内进行材料合成往往可以获得尺寸较小的物质,因此在纳米材料的制备上广泛应用.
电化学的方法了解的不多,我个人认为这两种方法在设计理念上还是有所区别的

A：
采用粘度法对微乳液的相对分子量进行了测定.分析了单体浓度、引发剂浓度、乳化剂浓度、温度和乳液pH值等反应条件对聚合产物相对分子质量的影响
Determination of the relative molecular mass of micro-emulsion was conducted by viscometry. The impact of various reactive conditions such as monomer concentration, initiator concentration, emulsifier concentration, temperature and the pH value of emulsion , on the relative molecular quality of polymerization products was also analyzed.
B：
本文研究了乳化剂、反应温度、反应时间对乳液冻融前后稳定性的影响.结果表明,当乳化剂的质量分数为4.0、反应温度为70-75℃,反应时间120min时乳液冻融稳定性较好.
This article studies the influence of emulsifier, reaction temperature and time on the stability of emulsion before and after freeze-thaw. The result shows that the freeze-thaw stability of emulsion is better when the mass fraction of emulsifier is 4.0, the reaction temperature is at 70-75℃ and the reaction time is 120 minutes.
【英语牛人团】

Atlas G-1441x05polyoxyethylene sorbitol 1anolin derivativex05聚氧乙烯山梨醇羊毛脂衍生物x05非离子x0514.0
Solulan C-24x05P.O.E.(24)cholesterolx05聚氧乙烯(24EO)胆固醇醚x05非离子x0514.0
Solulan PB-20x05P.O.P.(20)1anolin alcoholx05聚氧丙烯(20PO)羊毛醇醚x05非离子x0514.0
Atlas G-7596jx05polyoxyethylene sotbitan monolauratx05聚氧乙烯失水山梨醇单月桂酸酯x05非离子x0514.9
Tween 60x05polyoxyethylene sorbitan monostearatex05聚氧乙烯(20EO)失水山梨醇单硬脂酸酯x05非离子x0514.9
Ameroxol OE-20x05P.O.E.(20) oleyl alcoholx05聚氧乙烯(20EO)油醇醚x05非离子x0515.0
Glucamate SSE-20x05P.O.E.(20) Glucamate SSx05聚氧乙烯(20EO)甲基葡萄糖苷倍半油酸酯x05非离子x0515.0
Solulan 16x05P.O.E.(16) lanolin alcoholx05聚氧乙烯(16EO)羊毛醇醚x05非离子x0515.0
Solulan 25x05P.O.E.(25) lanolin alcoholx05聚氧乙烯(25EO)羊毛醇醚x05非离子x0515.0
Solulan 97x05Acetylated P.O.E.(20) lanolin Derivx05聚氧乙烯(9EO)乙酰化羊毛脂衍生物x05非离子x0515.0
Tween 80x05polyoxyethylene sorbitan monostearatex05聚氧乙烯(20EO)失水山梨醇单油酸酯x05非离子x0515.0
Myrj 49x05Polyoxyethylene monostearatx05聚氧乙烯单硬脂酸酯x05非离子x0515.0
Altlas G-2144x05Polyoxyethylene monooleatex05聚氧乙烯单油酸酯x05非离子x0515.1
Atlas G-3915x05polyoxyethylene oleyl etherx05聚氧乙烯油基醚x05非离子x0515.3
Atlas G-3720x05polyoxyethylene stearyl alcoholx05聚氧乙烯十八醇x05非离子x0515.3
Atlas G-3920x05polyoxyethylene oleyl alcoholx05聚氧乙烯油醇x05非离子x0515.4
Emulphor ON-870x05Polyoxyethylene fatty alcoholx05聚氧乙烯脂肪醇x05非离子x0515.4
Atlas G-2079x05polyoxyethylene glycol monopalmitatex05聚乙二醇单棕榈酸酯x05非离子x0515.5
Tween 40x05polyoxyethylene sorbitan monopalmitatex05聚氧乙烯(20EO)失水山梨醇单棕榈酸酯x05非离子x0515.6
Atlas G-3820x05Polyoxyethylene cetyl alcoholx05聚氧乙烯十六烷基醇x05非离子x0515.7
Atlas G-2162x05Polyoxyethylene oxypropylene stearatex05聚氧乙烯氧丙烯硬脂酸酯x05非离子x0515.7
Atlas G-1741x05Polyoxyethylene sorbitan lanolin derivativex05聚氧乙烯山梨醇羊毛脂衍生物x05非离子x0516.0
Myrj 51x05Polyoxyethylene monostearatex05聚氧乙烯单硬脂酸酯x05非离子x0516.0
Atlas G-7596Px05Polyoxyethylene sorbitan monolauratex05聚氧乙烯失水山梨醇单月桂酸酯x05非离子x0516.3
Atlas G-2129x05Polyoxyethylene monolauratex05聚氧乙烯单月桂酸酯x05非离子x0516.3
Atlas G-3930x05Polyoxyethylene oleyl etherx05聚氧乙烯油基醚x05非离子x0516.6
Tween 20x05Polyoxyethylene sorbitan monolauratex05聚氧乙烯(20EO)失水山梨醇单月桂酸酯x05非离子x0516.7
Brij 35x05Polyoxyethylene lauryl etherx05聚氧乙烯月桂醚x05非离子x0516.9
Myrj 52x05Polyoxyethylene monolauratex05聚氧乙烯单硬脂酸酯x05非离子x0516.9
Myrj 53x05Polyoxyethylene monolaurate x05聚氧乙烯单硬脂酸酯x05非离子x0517.9
－x05sodium oleatex05油酸钠x05阴离子x0518.0
Atlas G-2159x05Polyoxyethylene monolaurate x05聚氧乙烯单硬脂酸酯x05非离子x0518.8

通过反相微乳液制备的纳米颗粒一般为纳米颗粒,形态是分散的,需要按不材料的结晶温度,进行加热处理,才能形成晶体.如,TiO2材料350~500摄氏度处理一定时间,可获得锐钛矿型晶体.可能因为没有高温处理的原因,未形成晶体的材料不能出现峰值.

微乳液这个概念是1959 年由英国化学家J .H.
Schulman 提出来的[1 ] ,微乳液一般是由表面活性剂、助
表面活性剂、油与水等组分在适当比例下组成的五色、
透明(或半透明) 、低粘度的热力学体系.由于其具有
超低界面张力(10 - 10 - 7N/ m) 和很高的增溶能力(其
增溶量可达60 70 %) 的稳定热力学体系[2 - 3 ] .

电导率的显示同你测试溶液的温度有着很大的关系的.一般来说如果你的议器上没温度补偿的功能你测的时候会随着温度的变化而显示的数也会跟着变化的.我看你测的是微乳液干什么用的我就不知了,是不是你放置一些时候有沉淀发生而影响电导率了呢?电导率只能表现的是导电性其它的说明不了什么.其中的因素又会有多种影响.我不能一一说明太多了.

Alcohol as cosurfactant,oleic acid mixed with sodium oleate as surfactant agent, then we get the phase diagram,using diesel-water microemulsion prepared by dilution. The influences of different alcoh...

微乳液溶胶凝胶法是用含高化学活性组分的化合物作前驱体,在液相下将这些原料均匀混合,并进行水解、缩合化学反应,在溶液中形成稳定的透明溶胶体系,溶胶经陈化胶粒间缓慢聚合,形成三维空间网络结构的凝胶,凝胶网络间充满了失去流动性的溶剂,形成凝胶.凝胶经过干燥、烧结固化制备出分子乃至纳米亚结构的材料.
原理：
将酯类化合物或金属醇盐溶于有机溶剂中,形成均匀的溶液,然后加入其他组分,在一定温度下反应形成凝胶,最后经干燥处理制成产品.